| The heat-transferringprinting powder coating is a special kind ofpowder coating, specially used in bottom filmspraying in heat-transferring printing technology.The series products are the thermohardeningpowder coating that the material is based onthe function-changing polyester resin, curingagent and paint. It is suitable to use insideand outdoor. Through heat-transferring printingtechnology, it can form different pattern inbottom film, such as wood-like veins, marbleveins etc. At the same time, it can transfer-printany treated photos to the bottom film surface. | |
| The PowderPerformance | Application |
| Specific gravity: 1.4-1.8g/cm3(there is difference in different prescriptionand color) Granularity measuringthere is differencein different usage (average) (granularity) 99%＜100m 65%-70%＞32m See details in the requirement Packing: 20kg carton to pack, inside liningplastic bag | Epoxy polyester powdercoating is used in following
devicesCoronastatic spray coating/Triboelectricity
spraycoating/Static fluidized bed/Fluidized bed The coating film thicknessbetween 40-150m There is difference in different industrialrequirement The coveragethe film thickness60m under 11-13 sq. m. /kg There is difference in different type and color The coverage rate can be calculated by followingformula :specific gravity ×coating film thickness= g/sq.m. Softening pointin 75-95℃ (Koflermethod ) There is difference in different type and color |
| Storage Term | Baking condition |
| The storage term: under 35℃ for12 months The epoxy polyester powder coating must be storedin the dry condition of under 35℃. All containers after being used must be re-encapsulated,and be back to original package. | All baking conditions mean workpiecetemperature : Low temperature curingat 160℃ to solidify12 minutes Normal curingat 180℃ to solidify 18 minutes Fast curingat 200to solidify 10 minutes |
| Corrosion resistance | The mechanical performance |
| All tests adopt de-oil zinc phosphidetest sample plate, the film
thickness 100-120m,finished under lab conditions. Salt spray test: ASTM B117/GB1771-91: no affectionafter 500 hours, and the section erosion isless than 2mm. Hot and humid test: Bs. 3900 Part F2 1973: after5000 hours GB1740/79 (89): after 1000 hours The coating film is no affection and a littlepolish loss. | All tests adopt de-oil iron phosphidesample plate, the film
thickness 60-80m, finishedunder lab conditions. Pencil hardness ：GB/T6739-96 ：H-2H Adhesion ：GB/T9286-98 ：class 0-1 Bending test（spindle column）：GB/T6742-86 ：0 Cupping test ：GB/T9753-88 ：6mm Impact test ：GB/T1732-93 ：50kg.cm |
| Appearance | Chemical performance |
| The polish is based on the standardof ISO2813 or GB/T9754-88, to
measure by 60°anglegauge. Polishhighlight type80% Semi-polish: 40-60% Plain polish: 30%±5% To inquire the products specifications fromthe local sales agency Effect: smooth Wrinkle Special effect or follows requirement | All tests adopt de-oil zinc phosphidetest sample plate, the film
thickness 100-120m,finished under lab conditions. There is no affection after 12 months. Acid acetic acid solution 20% Sulphuric acid solution 30% Phosphoric acid solution 30% Lactic acid solution 10% Alkali sodium carbonate solution 10% Ammonia solution 10% Solvent aromatic mixing |
| Sanitation and safety | The application scope |
| It follows the requirement ofsafety datasheet as much as possible | It has the best durability tosuit outdoor building Doors and windows frame/Metal gate/Plating/Guardfence/House furniture |
| Notice | |
| Not to recommendto use it in outdoor The weatherability of epoxy polyester powdercoating is poor, and it has the problems ofcolor changing, fading and powdering. In orderto enhance the weatherability and thermo stabilityof powder coating, please to refer to the powdercoating datasheet of Xinyu Company. | |